# High Entropy Alloy Catalytic Action on MgH2 Hydrogen Storage Materials Source: [High Entropy Alloy Catalytic Action on MgH2 Hydrogen Storage Materials]() Collection index: [llms.txt]() Data updated: 2025-10-28T13:54:41.299Z Authors: S. K. Verma, S. S. Mishra, N. K. Mukhopadhyay, T. P. Yadav Published: 2023-07-23T06:39:25.000Z ## Abstract Magnesium hydride (MgH2) is the mostly used material for solid-state hydrogen storage. However, their slow kinetics and highly unfavorable thermodynamics make them unsuitable for the practical applications. The current study describes the unusual catalytic action of a new class of catalyst, a high-entropy alloy (HEA) of Al20Cr16Mn16Fe16Co16Ni16, on the de/re-hydrogenation properties of MgH2. The onset desorption temperature of MgH2 is reduced significantly from 376 {\\deg}C (for pristine MgH2) to 338 degC when it is catalyzed with a HEA-based catalyst. On the other hand, a fast de/re-hydrogenation kinetics of MgH2 was observed during the addition of HEA-based catalyst. It ab sorbs 6.1 wt% of hydrogen in just 2 minutes at a temperature of 300 degC under 10 atm hydrogen pressure and desorbs ~ 5.4 wt% within 40 minutes. At moderate temperatures and low pressure, the HEA-based catalyst reduced desorption temperatures and improved re-hydrogenation kinetics. Even after 25 cycles of de/re-hydrogenation, the storage capacity of MgH2 catalyzed with the leached version of HEA degrades negligibly. ## Recorded benchmark results A research result applies to its stated dataset, split, metric and evaluation configuration. Compare like-for-like settings, preserve the metric's unit and direction, and distinguish paper-reported results from independent reproduction. The best result recorded here is not a claim of exhaustive, current global coverage. ## Original sources and implementation [Original paper]() [PDF]()